hot corrosion behavior of cold-sprayed conicraly coating in na2so4 salt
Clicks: 136
ID: 194274
2016
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Popular Article
30.0
/100
136 views
28 readers
AI Quality Assessment
Not analyzed
Readership in this journal
PopularRanked #41 of 52 articles by views in adsorption science and technology
Most read
Least read
Bar heights use a square-root scale.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
CoNiCrAlY coatings were prepared by cold spray process. After deposition, the pre-oxidation treatment of the coating was performed by vacuum heat-treatment. The microstructure and phase constituent of coating were characterized by XRD, SEM and EDS. The hot corrosion behavior of as-sprayed and pre-oxidized CoNiCrAlY coatings in molten Na2SO4 at 900℃ was also studied. The results show that the as-sprayed coating presents a dense structure with low porosity (less than 0.28%, volume fraction) and low oxygen content (0.12%, mass fraction). Vacuum pre-oxidation treatment forms a continuous and dense α-Al2O3 layer on the coating surface, with an average thickness of about 0.26μm. As-sprayed and pre-oxidized coatings can protect the substrate from hot corrosion due to the formation of a continuous and dense α-Al2O3 layer. Moreover, the vacuum pre-oxidation treatment can alleviate the diffusion of S and O into coating, and thus the hot corrosion resistance of coating is improved. The damage of hot corrosion plays a more important role than high temperature oxidation. When corrosion in single Na2SO4 molten salt with the same temperature, the consumption speed of Al is two times of that in high temperate oxidation
| Reference Key |
lin-wei2016journalhot
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;ZHANG Lin-wei;WANG Lu;WANG Quan-sheng;LU Lei;NING Xian-jin |
| Journal | adsorption science and technology |
| Year | 2016 |
| DOI |
10.11868/j.issn.1001-4381.2016.11.007
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.