synthesis and characterization of linio2 nanopowder with various chelating agents
Clicks: 112
ID: 188358
2010
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Popular Article
30.0
/100
112 views
18 readers
AI Quality Assessment
Not analyzed
Readership in this journal
PopularRanked #365 of 443 articles by views in reproductive biology and endocrinology
Most read
Least read
Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 443 in total.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
LiNiO2 powders were synthesized with acrylic acid, citric acid, oxalic acid, and triethanolamine (TEA) as a chelating agent. Crystallized LiNiO2 was synthesized in air at a calcinations temperature of 500∘C for 12 hours, when the molar ratio of chelating agents to total metal ion (RPM) was 1.0. The TEA-assisted method had the highest intensity ratio of (003)/(104) peaks of X-ray diffraction (XRD) spectrum. The transmission electron microscopy (TEM) analysis indicates that the sample prepared with triethanolamine obtained the smallest particle size with average particle size of only 12 nm. The results indicate that chelating agents have an important role in the intensity ratio of (003)/(104) peaks of XRD spectrum, size and shape of powders.
| Reference Key |
balandeh2010journalsynthesis
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;Mehrdad Balandeh;Sirous Asgari |
| Journal | reproductive biology and endocrinology |
| Year | 2010 |
| DOI |
10.1155/2010/695083
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.