composite coatings of titanium-aluminum nitride for steel against corrosion induced by solid nacl deposit and water vapor at 600 °c
Clicks: 276
ID: 185257
2004
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Steady Performance
30.0
/100
276 views
22 readers
AI Quality Assessment
Not analyzed
Readership in this journal
SteadyRanked #32 of 96 articles by views in Majalah Ilmiah Teknologi Elektro
Most read
Least read
Bar heights use a square-root scale.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
Composite coatings (Ti,Al)N with different Al content were deposited on a wrought martensite steel 1Cr11Ni2W2MoV by reactive multi-arc ion plating. With the addition of Al to the coatings, the crystallographic structure of them changed from B1 NaCl to B4 ZnS, the relevant hardness and adhesive strength firstly increased then decreased and their oxidation-resistance was also dramatically improved. It was indicated that the introduction of Al was beneficial to (Ti,Al)N coatings against corrosion induced by NaCl(s) in wet oxygen at 600 °C as well as wet corrosion in NaCl solution at ambient temperature.
| Reference Key |
li2004materialscomposite
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;M.S. Li;F.H. Wang;Y.H. Shu;W.T. Wu |
| Journal | Majalah Ilmiah Teknologi Elektro |
| Year | 2004 |
| DOI |
10.1590/S1516-14392004000100005
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.