ta/tio2-and nb/tio2-mixed oxides as efficient solar photocatalysts: preparation, characterization, and photocatalytic activity
Clicks: 199
ID: 181252
2012
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Popular Article
30.0
/100
199 views
26 readers
AI Quality Assessment
Not analyzed
Readership in this journal
PopularRanked #67 of 251 articles by views in construction and building materials
Most read
Least read
Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 251 in total.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
Ta/TiO2- and Nb/TiO2-mixed oxides photocatalysts were prepared by simple impregnation method at different TiO2 : Nb or Ta mass ratios of 1 : 0.1, 1 : 0.5, and 1 : 1, followed by calcination at 500∘C. The prepared powders have been characterized by XRD, XPS, UV-Vis spectra, and SEM. The photocatalytic activity was evaluated under natural solar light for decolorization and mineralization of azo dye Orange II solution. The results showed that Nb/TiO2- and Ta/TiO2-mixed oxides have higher activity than the untreated TiO2 under natural solar light. The maximum activity was observed for Nb/TiO2 sample (at mass ratio of 1 : 0.1), which is characterized by the smallest crystalline size (17.79 nm). Comparing with the untreated TiO2, the solar decolorization and mineralization rates improved by about 140% and 237%, respectively, and the band gap reduced to 2.80 eV. The results suggest that the crystal lattices of TiO2 powder are locally distorted by incorporating Nb5+ species into TiO2, forming a new band energy structure, which is responsible for the absorption in the visible region. Unlike Ta/TiO2, the Nb/TiO2-mixed oxides can prevent the grain size growth of the treated TiO2, which is important to achieve high solar photoactivity.
| Reference Key |
znad2012internationalta/tio2-and
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;Hussein Znad;Ming H. Ang;Moses O. Tade |
| Journal | construction and building materials |
| Year | 2012 |
| DOI |
10.1155/2012/548158
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.