effect of latent heat during primary crystallization on the nanostructural formation process in nanocrystalline soft magnetic materials
Clicks: 167
ID: 173349
2020
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Emerging Content
30.0
/100
167 views
33 readers
AI Quality Assessment
Not analyzed
Readership in this journal
EmergingRanked #23 of 51 articles by views in journal of hydrology: x
Most read
Least read
Bar heights use a square-root scale.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
Nanocrystalline soft magnetic materials are known to be prepared by primary crystallization of Fe-based amorphous precursors. Since the crystallization reaction is exothermic, the amorphous precursor may experience a temporary rise in its temperature relative to its surroundings during the process of nanocrystallization. Given the typical latent heat of primary crystallization (∼ 100 kJ/kg), this temperature rise may exceed hundreds of degrees if not adequately controlled and thus, lead to the formation of unwanted magnetically hard compounds. This effect is generally small for isolated ribbons annealed with a moderate heating rate. However, the recent adoption of high heating rates and short annealing times has caused the self-heating effect to become relevant even for small sample sizes. In this work, the effect of self-heating on the microstructure and magnetic properties of nanocrystalline Fe86B14 is investigated. It is found that magnetically hard Fe-B compounds cannot be avoided when annealing under vacuum in an infrared furnace with a heating rate ≥3 K/s due to the self-heating effect. However, the high thermal conductivity of the copper blocks used by the ultra-rapid annealing process can successfully prevent a self-heating induced temperature rise during annealing, avoiding unwanted compound formation. Finite Element Analysis is also used for predicting the extent of self-heating during infrared annealing.
| Reference Key |
parsons2020aipeffect
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;R. Parsons;B. Zang;H. Huang;H. Kishimoto;T. Shoji;A. Kato;K. Suzuki |
| Journal | journal of hydrology: x |
| Year | 2020 |
| DOI |
10.1063/1.5130427
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.