correlation of weld appearance with microstructure and mechanical properties of 2024-t4 aluminum alloy welded by fiber laser with filler wire
Clicks: 211
ID: 169742
2017
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Steady Performance
30.0
/100
211 views
46 readers
AI Quality Assessment
Not analyzed
Readership in this journal
SteadyRanked #28 of 52 articles by views in adsorption science and technology
Most read
Least read
Bar heights use a square-root scale.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
Two typical cross-section of welds, including nail shape and near X shape, are obtained in the process of fiber laser welding 2024-T4 Al alloy with filler wire. The correlations of the two weld appearances and other elements (such as microstructure, microhardness, and joint's tensile properties) were analyzed. The results show that the weld with near X shape cross-section during the welding process is more stable than that with nail shape cross-section, and the welding spatter of the former is smaller than that of the latter. The microstructure of the weld zone is columnar grains and equiaxed grains, the columnar grains are formed near the fusion line and growing along the vertical direction of the fusion line, the equiaxed grains are distributed in the center of the weld zone. The secondary dendrite of the grains in the center of the weld with nail shape cross-section grows better, and gradually forms to equiaxed dendrite, while the grains size of the weld with near X shape cross-section is relatively finer, exhibiting equiaxed cellular grain. Compared with the joint with nail shape cross-section of the weld, the joint with near X shape cross-section of the weld have some different characteristics, the precipitation strengthening phase θ(Al2Cu) content in weld zone of the latter is more than that of the former, the average microhardness value of the weld zone of the latter is higher than that of the former, the softening phenomenon of heat affect zone (HAZ) of the latter is weaker than that of the former, and the joint's tensile strength and plasticity of the latter are lower than that of the former slightly.
| Reference Key |
fei2017journalcorrelation
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;XU Fei;CHEN Li;HE En-guang;GUO Lu-yun |
| Journal | adsorption science and technology |
| Year | 2017 |
| DOI |
10.11868/j.issn.1001-4381.2015.001071
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.