the preparation and characterization of β-sialon nanostructure whiskers
Clicks: 4
ID: 165510
2008
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Star Article
0.9
/100
4 views
3 readers
AI Quality Assessment
Not analyzed
Readership in this journal
StarRanked #432 of 443 articles by views in reproductive biology and endocrinology
Most read
Least read
Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 443 in total.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
Two kinds of β-SiAlON nanostructure whiskers, rod-like and wool-like whiskers, were synthesized by pressure-less sintering method at 1773 K for 5 hours. The whiskers synthesized were characterized by powder X-ray diffraction (XRD), scanning electron microscope (SEM), transmission electron microscope (TEM), and high-resolution electron microscope (HREM) techniques. It was found that diameter distribution of rod-like whiskers was about 80–250 nm, while it was about 45–55 nm in diameter for the wool-like whiskers. The growth mechanisms of β-SiAlON nanostructure whiskers are discussed by the vapor-solid (VS) and vapor-liquid-solid (VLS) mechanisms, respectively.
| Reference Key |
dong2008journalthe
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;Pengli Dong;Xidong Wang;Mei Zhang;Min Guo;Seshadri Seetharaman |
| Journal | reproductive biology and endocrinology |
| Year | 2008 |
| DOI |
10.1155/2008/282187
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.