high temperature deformation behavior of 8090 al-li alloy

Clicks: 127
ID: 162555
2013
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This article has not been analysed, so there is no overall score — reader engagement is measured and shown alongside.
AI Quality Assessment
Not analyzed
Readership in this journal
Popular

Ranked #182 of 254 articles by views in bulletin of the korean chemical society

Most read Least read

Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 254 in total.

Mint this article as an NFT
Not yet minted

Create a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.

5 SUSD one-off · no wallet required
Abstract
High temperature deformation behavior, especially the superplasticity of an 8090 Al-Li alloy, was studied within the recent framework of the internal variable theory of structural superplasticity. In this study, a series of load relaxation tests were conducted at various temperatures ranging from 200°C to 530°C to obtain the flow curves of log ε˙ versus log ε. The effect of grain size was also examined by varying the grain sizes through a proper thermomechanical treatment. The flow curves were found to be composite curves consisting of contributions from grain boundary sliding (GBS) and grain matrix deformation (GMD) at superplastic temperatures. The activation energy obtained for GMD was 124.9 kJ/mole in the temperature range from 470°C to 530°C, very similar to that for self-diffusion in pure Al.
Reference Key
jung2013advanceshigh Use this key to autocite in the manuscript while using SciMatic Manuscript Manager or Thesis Manager
Authors ;Woo Young Jung;Tae Kwon Ha
Journal bulletin of the korean chemical society
Year 2013
DOI
10.1155/2013/512606
URL
Keywords

Citations

No citations found. To add a citation, contact the admin at info@scimatic.org

No comments yet. Be the first to comment on this article.