preparation and performance of modified red mud-based catalysts for selective catalytic reduction of nox with nh3

点击量: 229
ID: 161102
2018
免费 PDF
文章质量与表现指标
综合质量
Not rated
Combines reader engagement with the AI quality analysis. This article has not been analysed, so there is no overall score — reader engagement is measured and shown alongside.
AI质量评估
未分析
Readership in this journal
Emerging

Ranked #61 of 89 articles by views in journal of essential oil research

Most read Least read

Bar heights use a square-root scale.

Mint this article as an NFT
Not yet minted

Create a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.

5 SUSD one-off · no wallet required
Sign in to mint
摘要
Bayer red mud was selected, and the NH3-SCR activity was tested in a fixed bed in which the typical flue gas atmosphere was simulated. Combined with XRF, XRD, BET, SEM, TG and NH3-Temperature Programmed Desorption (TPD) characterization, the denitration characteristics of Ce-doped red mud catalysts were studied on the basis of alkali-removed red mud. The results showed that typical red mud was a feasible material for denitration catalyst. Acid washing and calcining comprised the best treatment process for raw red mud, which reduced the content of alkaline substances, cleared the catalyst pore and optimized the particle morphology with dispersion. In the temperature range of 300–400 °C, the denitrification efficiency of calcined acid washing of red mud catalyst (ARM) was more than 70%. The doping of Ce significantly enhanced NH3 adsorption from weak, medium and strong acid sites, reduced the crystallinity of α-Fe2O3 in ARM, optimized the specific surface area and broadened the active temperature window, which increased the NOx conversion rate by an average of nearly 20% points from 250–350 °C. The denitration efficiency of Ce0.3/ARM at 300 °C was as high as 88%. The optimum conditions for the denitration reaction of the Ce0.3/ARM catalyst were controlled as follows: Gas Hourly Space Velocity (GHSV) of 30,000 h−1, O2 volume fraction of 3.5–4% and the NH3/NO molar ratio ([NH3/NO]) of 1.0. The presence of SO2 in the feed had an irreversible negative effect on the activity of the Ce0.3/ARM catalyst.
参考键
wu2018catalystspreparation 使用此键在稿件中自动引用，同时使用 SciMatic 稿件管理器或论文管理器
作者 ;Jingkun Wu;Zhiqiang Gong;Chunmei Lu;Shengli Niu;Kai Ding;Liting Xu;Kang Zhang
期刊 journal of essential oil research
年份 2018
DOI
10.3390/catal8010035
URL
http://www.mdpi.com/2073-4344/8/1/35
关键词
red mud ceriumchemical technologychemistry

引用

未找到引用。如需添加引用，请联系管理员 info@scimatic.org

评论

暂无评论。成为第一个评论此文章的人。