development of a tic/cr23c6 composite coating on a 304 stainless steel substrate through a tungsten inert gas process
Clicks: 327
ID: 160517
2017
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Steady Performance
30.0
/100
327 views
57 readers
AI Quality Assessment
Not analyzed
Readership in this journal
SteadyRanked #11 of 58 articles by views in die pharmazie
Most read
Least read
Bar heights use a square-root scale.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
The aim of this study was to develop a composite coating on 304 stainless steel employing a TIG (tungsten inert gas) process. Ti wire cored with graphite powder was used as the means of coating material. The process parameters were controlled to develop a coating with optimum characteristics (i.e., hardness and wear resistance). The microstructure of the coating was analyzed with SEM and XRD. It was found that both the hardness and the wear resistance increase as the current increases, while both of these properties decrease as travelling speed increases. It was found that the coated samples with composite layers were harder than the substrate and can range up to 1100 HV, almost 4.5 times higher than the hardness of 304 stainless steel. Likewise, the wear resistance of the coating was observed to be 4.5 times higher than that of the substrate. The high performance of the coating, as revealed by microstructural analysis, was due to the formation of TiC and Cr23C6.The optimum conditions for producing the coating are thus proposed to include a 120 A current and a 3.17 mm/s travel speed.
| Reference Key |
heidarshenas2017coatingsdevelopment
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;Behzad Heidarshenas;Ghulam Hussain;Mohammed. Bsher. A. Asmael |
| Journal | die pharmazie |
| Year | 2017 |
| DOI |
10.3390/coatings7060080
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.