structure analysis of copt alloy film with metastable ordered phases of l11 and bh formed on ru(0001) underlayer
Clicks: 173
ID: 156548
2014
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Steady Performance
30.0
/100
173 views
32 readers
AI Quality Assessment
Not analyzed
Readership in this journal
SteadyRanked #80 of 625 articles by views in utilitas mathematica
Most read
Least read
Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 625 in total.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
CoPt alloy films of 40 nm thickness are prepared on MgO(111) substrates with and without Ru(0001) underlayer at 300 °C by radio-frequency magnetron sputtering. CoPt films with the close-packed plane parallel to the substrate surface grow epitaxially on the Ru underlayer as well as on the MgO substrate. Flat surfaces with the arithmetical mean roughness value of 0.2 nm are realized for both films. The crystal structure is determined by considering the atomic stacking sequence of close-packed plane and the order degree. The film formed on MgO substrate consists of an fcc-based L11 ordered crystal, whereas the film grown on Ru underlayer involves an hcp-based Bh ordered crystal in addition to the L11 ordered crystal. The order degrees of films formed on MgO substrate and Ru underlayer are 0.30 and 0.34, respectively. The L11 crystal consists of two variants whose stacking sequences of close-packed plane are ABCABC… and ACBACB…, while the Bh crystal is a single-crystal with the stacking sequence of ABAB… Formation of Bh crystal is promoted on the Ru underlayer. The film formed on Ru underlayer shows a strong perpendicular magnetic anisotropy reflecting the magnetocrystalline anisotropies of L11 and Bh crystals.
| Reference Key |
mitsuru2014epjstructure
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;Ohtake Mitsuru;Suzuki Daisuke;Kirino Fumiyoshi;Futamoto Masaaki |
| Journal | utilitas mathematica |
| Year | 2014 |
| DOI |
10.1051/epjconf/20147506003
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.