hybrid inorganic-organic nano- and microcomposites based on silica sols and synthetic polyelectrolytes
Clicks: 240
ID: 154893
2008
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Popular Article
30.0
/100
240 views
58 readers
AI Quality Assessment
Not analyzed
Readership in this journal
PopularRanked #64 of 74 articles by views in introducing the mysql 8 document store
Most read
Least read
Bar heights use a square-root scale.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
Interaction between anionic (and cationic) colloidal particles of silica having the particles diameters 12 and 22 nm with synthetic cationic (and anionic) polyelectrolytes of various nature and structure was studied by potentiometric, conductimetric spectroturbidimetric and viscometric methods in aqueous solution. It was shown that the complexation of silica nanoparticles with linear polyelectrolytes leads to formation of mostly stoichiometric interpolyelectrolyte complexes (IPEC) which precipitate from aqueous solution. Casting of water-soluble IPEC followed by thermal treatment gives thin composite films insoluble in water while ‘layer by layer’ (LbL) deposition of polyelectrolyte components onto silica sols leads to formation of multilayered nano- and microcomposites. The possible mechanism of formation of LbL multilayers consisting of silica sol (SiO2) ‘cores’ and polyethyeleneimine-polyacrylic acid (PEI-PAA) ‘shells’ was suggested. It was found that in diluted aqueous solution the radius of gyration, Rg and hydrodynamic radius, Rhmean of LbL particles are independent on LbL concentration and smaller than 100 nm. The zeta potential values of LbL particles are arranged between –10 and –30 mV. The average size of LbL particles estimated by scanning electron microscopy (SEM) is in the range of 200–500 nm. Thermal treatment of LbL multilayers followed by etching of (SiO2) ‘core’ by HF leads to formation of a series of spherical nanocavities and blob-like microcavities.
| Reference Key |
noauthor2008expresshybrid
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ; |
| Journal | introducing the mysql 8 document store |
| Year | 2008 |
| DOI |
10.3144/expresspolymlett.2008.14
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.