off-axial tensile properties of precontraint pvdf coated polyester fabrics under different tensile rates
Clicks: 277
ID: 153072
2016
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Steady Performance
30.0
/100
277 views
51 readers
AI Quality Assessment
Not analyzed
Readership in this journal
SteadyRanked #17 of 254 articles by views in bulletin of the korean chemical society
Most read
Least read
Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 254 in total.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
Two types of Precontraint PVDF coated polyester are taken as the research objects. A series of uniaxial tensile tests were carried out to study the tensile performances of the specimens in eleven in-plane directions including 0°, 5°, 15°, 25°, 35°, 45°, 55°, 65°, 75°, 85°, and 90°, and six tensile rates (10 mm/min, 25 mm/min, 50 mm/min, 100 mm/min, 200 mm/min, and 500 mm/min) were also considered. The corresponding failure modes and fracture mechanisms were discussed, and the relationships between tensile strength and strain at break and tensile rate and off-axial angles were obtained. Results show that the Precontraint PVDF coated woven fabrics are typically anisotropic. With off-axial angle increasing, the tensile strength decreases while the strain at break increases. Three failure modes can be observed, including failure of yarns pulled out, yarns fracture, and mixture failure. With tensile rate increasing, the tensile strength increases slightly while the strain at break decreases. The tensile strength and strain at break show good linear relationship with tensile rate’s logarithm.
| Reference Key |
zhang2016advancesoff-axial
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;Lanlan Zhang |
| Journal | bulletin of the korean chemical society |
| Year | 2016 |
| DOI |
10.1155/2016/9856474
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.