effect of partial cladding pattern of aluminum 7075 t651 on corrosion and mechanical properties
Clicks: 147
ID: 147883
2017
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Steady Performance
30.0
/100
147 views
18 readers
AI Quality Assessment
Not analyzed
Readership in this journal
SteadyRanked #149 of 254 articles by views in bulletin of the korean chemical society
Most read
Least read
Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 254 in total.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
The corrosion resistance of aluminum 7075 T651 in full clad (Alclad), partial clad, and bare (unclad) forms was compared after 300 hours of corrosion exposure in an acidic salt spray cabinet test at 36°C. After corrosion exposure, severe to moderate exfoliation corrosion was observed on the unprotected medium sized test panel, light general corrosion was observed on the partially clad panel, and patches of corrosion not penetrating the clad layer were observed on the fully clad panel. After corrosion tests, the tensile strength of partially clad, fully clad, and unprotected panels decreased by 3.4%, 4.0%, and 5.3%, respectively.
| Reference Key |
rendell2017advanceseffect
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;E. Rendell;A. Hsiao;J. Shirokoff |
| Journal | bulletin of the korean chemical society |
| Year | 2017 |
| DOI |
10.1155/2017/5282659
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.