kinetics of co oxidation over unloaded and pd-loaded α-fe2o3 spherical submicron powder catalysts: photoacoustic investigations at low pressure

Clicks: 151
ID: 144875
2018
Free PDF
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This article has not been analysed, so there is no overall score — reader engagement is measured and shown alongside.
AI Quality Assessment
Not analyzed
Readership in this journal
Steady

Ranked #79 of 89 articles by views in journal of essential oil research

Most read Least read

Bar heights use a square-root scale.

Mint this article as an NFT
Not yet minted

Create a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.

5 SUSD one-off · no wallet required
Sign in to mint
Abstract
In this study, α-Fe2O3 spherical particles with an average diameter of approximately 200 nm were synthesized by a solvothermal method for use as both a catalyst and medium for a Pd catalyst. The kinetics of CO oxidation over powders of α-Fe2O3 spherical particles and 14 wt % Pd/α-Fe2O3 spherical particles were measured in a static reactor by using a CO2 laser-based photoacoustic technique. The total pressure was fixed at 40 Torr for the CO/O2/N2 mixture for temperatures in the range of 225–350 °C. The variation in the CO2 photoacoustic signal with the CO2 concentration during CO oxidation was recorded as a function of time, and the CO2 photoacoustic data at the early reaction stage was used to estimate the rates of CO2 formation. Based on plots of ln(rate) vs. 1/T, apparent activation energies were calculated as 13.4 kcal/mol for the α-Fe2O3 submicron powder and 13.2 kcal/mol for the 14 wt % Pd/α-Fe2O3 submicron powder. Reaction orders with respect to CO and O2 were determined from the rates measured at various partial pressures of CO and O2 at 350 °C. The zero-order of the reaction with respect to Po2 was observed for CO oxidation over α-Fe2O3 submicron powder, while 0.48 order to Po2 was observed for CO oxidation over Pd/α-Fe2O3 submicron powder. The partial orders with respect to PCO were determined as 0.58 and 0.54 for the α-Fe2O3, and the Pd/α-Fe2O3 submicron powders, respectively. The kinetic results obtained from both catalysts were compared with those for the α-Fe2O3 fine powder catalysts and were used to understand the reaction mechanism.
Reference Key
roh2018catalystskinetics Use this key to autocite in the manuscript while using SciMatic Manuscript Manager or Thesis Manager
Authors ;Joong-Seok Roh;Ji-Yeong Kim;Joong-Gill Choi;Sung-Han Lee
Journal journal of essential oil research
Year 2018
DOI
10.3390/catal8030098
URL
http://www.mdpi.com/2073-4344/8/3/98
Keywords Keywords not found

Citations

No citations found. To add a citation, contact the admin at info@scimatic.org

Comments

No comments yet. Be the first to comment on this article.