characterization of anion exchange membrane containing epoxy ring and c–cl bond quaternized by various amine groups for application in fuel cells
Clicks: 282
ID: 143124
2015
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Popular Article
30.0
/100
282 views
51 readers
AI Quality Assessment
Not analyzed
Readership in this journal
PopularRanked #79 of 526 articles by views in acs combinatorial science
Most read
Least read
Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 526 in total.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
Anion exchange membranes were synthesized from different compositions of glycidyl methacrylate (GMA) and vinylbenzyl chloride (VBC), with constant content of divinyl benzene (DVB) by radical polymerization using benzoyl peroxide (BPO) on non-woven polyethylene terephthalate (PET) substrate. Polymerized membranes were then quaternized by soaking in trimethylamine (TMA), triethylamine (TEA), tripropylamine (TPA), and 1,4-diazabicyclo [2.2.2] octane (DABCO). Characteristics of membranes were confirmed by Fourier transform infrared spectroscopy, water uptake, ion exchange capacity, ion conductivity, thermal, and alkaline stability. The results revealed that membranes quaternized by TPA and DABCO showed high affinity when GMA content was 15 wt% and 75 wt%, respectively. IEC and ion conductivity of membranes quaternized by TPA were 1.34 meq·g−1 and 0.022 S·cm−1 (at 60 °C), respectively. IEC and ion conductivity of membranes were quaternized by DABCO were 1.34 meq·g−1 and 0.021 S·cm−1 (at 60 °C), respectively. The results indicate that the membrane containing GMA 15 wt% quaternized by TPA showed the highest thermal stability among membranes and exhibited high ion conductivity compared to existing researches using GMA, VBC, and DVB monomers.
| Reference Key |
jeong2015energiescharacterization
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;Sung Kuk Jeong;Ju Sung Lee;Sahng Hyuck Woo;Jin Ah Seo;Byoung Ryul Min |
| Journal | acs combinatorial science |
| Year | 2015 |
| DOI |
10.3390/en8077084
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.