multi-alkenylsilsesquioxanes as comonomers and active species modifiers of metallocene catalyst in copolymerization with ethylene
Cliques: 300
ID: 139327
2018
Metricas de Qualidade e Desempenho do Artigo
Qualidade Geral
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Engajamento do Leitor
Steady Performance
30.0
/100
300 visualizacoes
72 leitores
Avaliacao de Qualidade por IA
Nao analisado
Readership in this journal
SteadyRanked #61 of 194 articles by views in Journal of Fluorescence
Most read
Least read
Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 194 in total.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Resumo
The copolymers of ethylene (E) with open-caged iso-butyl-substituted tri-alkenyl-silsesquioxanes (POSS-6-3 and POSS-10-3) and phenyl-substituted tetra-alkenyl-silsesquioxane (POSS-10-4) were synthesized by copolymerization over the ansa-metallocene catalyst. The influence of the kind of silsesquioxane and of the copolymerization conditions on the reaction performance and on the properties of the copolymers was studied. In the case of copolymerization of E/POSS-6-3, the positive comonomer effect was observed, which was associated with the influence of POSS-6-3 on transformation of the bimetallic ion pair to the active catalytic species. Functionality of silsesquioxanes and polymerization parameters affected the polyhedral oligomeric silsesquioxanes (POSS) contents in the copolymers which varied in the range of 1.33–7.43 wt %. Tri-alkenyl-silsesquioxanes were incorporated into the polymer chain as pendant groups while the tetra-alkenyl-silsesquioxane derivative could act as a cross-linking agent which was proved by the changes in the contents of unsaturated end groups, by the glass transition temperature values, and by the gel contents (up to 81.3% for E/POSS-10-4). Incorporation of multi-alkenyl-POSS into the polymer chain affected also the melting and crystallization behaviors.
| Chave de Referencia |
groch2018polymersmulti-alkenylsilsesquioxanes
Use esta chave para citacao automatica no manuscrito ao usar
SciMatic Gerenciador de Manuscritos ou Gerenciador de Teses
|
|---|---|
| Autores | ;Paweł Groch;Katarzyna Dziubek;Krystyna Czaja;Katarzyna Mituła;Beata Dudziec |
| Periodico | Journal of Fluorescence |
| Ano | 2018 |
| DOI |
10.3390/polym10020223
|
| URL | |
| Palavras-chave |
Citacoes
Nenhuma citacao encontrada. Para adicionar uma citacao, entre em contato com o administrador em info@scimatic.org
Comentarios
Nenhum comentario ainda. Seja o primeiro a comentar neste artigo.