effect of molybdenum on the corrosion behavior of high-entropy alloys cocrfeni2 and cocrfeni2mo0.25 under sodium chloride aqueous conditions
Clicks: 242
ID: 138848
2018
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Emerging Content
30.0
/100
242 views
20 readers
AI Quality Assessment
Not analyzed
Readership in this journal
EmergingRanked #31 of 254 articles by views in bulletin of the korean chemical society
Most read
Least read
Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 254 in total.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
The corrosion behavior of high-entropy alloys (HEAs) CoCrFeNi2 and CoCrFeNi2Mo0.25 was investigated in 3.5 wt. percent sodium chloride (NaCl) at 25°C by electrochemical methods. Their corrosion parameters were compared to those of HASTELLOY® C-276 (UNS N10276) and stainless steel 316L (UNS 31600) to assess the suitability of HEAs for potential industrial applications in NaCl simulating seawater type environments. The corrosion rates were calculated using corrosion current determined from electrochemical experiments for each of the alloys. In addition, potentiodynamic polarization measurements can indicate active, passive, and transpassive behavior of the metal as well as potential susceptibility to pitting corrosion. Cyclic voltammetry (CV) can confirm the alloy susceptibility to pitting corrosion. Electrochemical impedance spectroscopy (EIS) elucidates the corrosion mechanism under studied conditions. The results of the electrochemical experiments and scanning electron microscopy (SEM) analyses of the corroded surfaces revealed general corrosion on alloy CoCrFeNi2Mo0.25 and HASTELLOY C-276 and pitting corrosion on alloy CoCrFeNi2 and stainless steel 316L.
| Reference Key |
rodriguez2018advanceseffect
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;Alvaro A. Rodriguez;Joseph H. Tylczak;Michael C. Gao;Paul D. Jablonski;Martin Detrois;Margaret Ziomek-Moroz;Jeffrey A. Hawk |
| Journal | bulletin of the korean chemical society |
| Year | 2018 |
| DOI |
10.1155/2018/3016304
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.