experimental investigation and discussion on the mechanical endurance limit of nafion membrane used in proton exchange membrane fuel cell

Clicks: 175
ID: 135529
2014
Free PDF
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This article has not been analysed, so there is no overall score — reader engagement is measured and shown alongside.
AI Quality Assessment
Not analyzed
Readership in this journal
Popular

Ranked #324 of 526 articles by views in acs combinatorial science

Most read Least read

Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 526 in total.

Mint this article as an NFT
Not yet minted

Create a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.

5 SUSD one-off · no wallet required
Sign in to mint
Abstract
As a solution of high efficiency and clean energy, fuel cell technologies, especially proton exchange membrane fuel cell (PEMFC), have caught extensive attention. However, after decades of development, the performances of PEMFCs are far from achieving the target from the Department of Energy (DOE). Thus, further understanding of the degradation mechanism is needed to overcome this obstacle. Due to the importance of proton exchange membrane in a PEMFC, the degradation of the membrane, such as hygrothermal aging effect on its properties, are particularly necessary. In this work, a thick membrane (Nafion N117), which is always used as an ionic polymer for the PEMFCs, has been analyzed. Experimental investigation is performed for understanding the mechanical endurance of the bare membranes under different loading conditions. Tensile tests are conducted to compare the mechanical property evolution of two kinds of bare-membrane specimens including the dog-bone and the deeply double edge notched (DDEN) types. Both dog-bone and DDEN specimens were subjected to a series of degradation tests with different cycling times and wide humidity ranges. The tensile tests are repeated for both kinds of specimens to assess the strain-stress relations. Furthermore, Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD) and Scanning electron microscope (SEM) observation and water absorption measurement were conducted to speculate the cause of this variation. The initial cracks along with the increasing of bound water content were speculated as the primary cause.
Reference Key
xiao2014energiesexperimental Use this key to autocite in the manuscript while using SciMatic Manuscript Manager or Thesis Manager
Authors ;Yang Xiao;Chongdu Cho
Journal acs combinatorial science
Year 2014
DOI
10.3390/en7106401
URL
http://www.mdpi.com/1996-1073/7/10/6401
Keywords Keywords not found

Citations

No citations found. To add a citation, contact the admin at info@scimatic.org

Comments

No comments yet. Be the first to comment on this article.