Investigation of the Structural, Electrical, and Optical Properties of the Nano-Scale GZO Thin Films on Glass and Flexible Polyimide Substrates

Clicks: 341
ID: 12406
2016
Free PDF
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This article has not been analysed, so there is no overall score — reader engagement is measured and shown alongside.
AI Quality Assessment
Not analyzed
Readership in this journal
Popular

Ranked #71 of 331 articles by views in Nanomaterials

Most read Least read

Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 331 in total.

Mint this article as an NFT
Not yet minted

Create a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.

5 SUSD one-off · no wallet required
Sign in to mint
Abstract
In this study, Ga2O3-doped ZnO (GZO) thin films were deposited on glass and flexible polyimide (PI) substrates at room temperature (300 K), 373 K, and 473 K by the radio frequency (RF) magnetron sputtering method. After finding the deposition rate, all the GZO thin films with a nano-scale thickness of about 150 ± 10 nm were controlled by the deposition time. X-ray diffraction patterns indicated that the GZO thin films were not amorphous and all exhibited the (002) peak, and field emission scanning electron microscopy showed that only nano-scale particles were observed. The dependences of the structural, electrical, and optical properties of the GZO thin films on different deposition temperatures and substrates were investigated. X-ray photoemission spectroscopy (XPS) was used to measure the elemental composition at the chemical and electronic states of the GZO thin films deposited on different substrates, which could be used to clarify the mechanism of difference in electrical properties of the GZO thin films. In this study, the XPS binding energy spectra of Ga2p3/2 and Ga2p1/2 peaks, Zn2p3/2 and Zn2p1/2 peaks, the Ga3d peak, and O1s peaks for GZO thin films on glass and PI substrates were well compared.
Reference Key
wang2016investigationnanomaterials Use this key to autocite in the manuscript while using SciMatic Manuscript Manager or Thesis Manager
Authors Wang, Fang-Hsing;Chen, Kun-Neng;Hsu, Chao-Ming;Liu, Min-Chu;Yang, Cheng-Fu;
Journal Nanomaterials
Year 2016
DOI
DOI not found
URL
http://www.mdpi.com/2079-4991/6/5/88
Keywords Keywords not found

Citations

No citations found. To add a citation, contact the admin at info@scimatic.org

Comments

No comments yet. Be the first to comment on this article.