Enhancement in Nanomechanical, Thermal, and Abrasion Properties of SiO2 Nanoparticle-Modified Epoxy Coatings
Clicks: 279
ID: 118753
2020
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Steady Performance
30.0
/100
279 views
22 readers
AI Quality Assessment
Not analyzed
Readership in this journal
SteadyRanked #19 of 39 articles by views in coatings
Most read
Least read
Bar heights use a square-root scale.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
Epoxy formulations containing 1%, 3%, and 5% SiO2 nanoparticles (SNPs) were produced and applied to mild steel substrates in order to improve their thermal, nanomechanical, and abrasion resistance. Field emission scanning electron microscopy (FE-SEM) was used to analyze the dispersion of nanoparticles in the final coating samples, and Energy-dispersive X-ray spectroscopy (EDX) was used to confirm the presence of nanoparticles. Thermogravimetric analysis (TGA) was employed to measure the thermal resistance of the prepared coatings. Conventional techniques were used to measure the impact and scratch resistance. For nanomechanical testing, nanoindentation was performed using a Berkovich-type indenter. Using a taber abraser, the abrasion properties of the coatings were measured. The FE-SEM images indicated good dispersion of the nanoparticles at all three different loading levels. The scratch, impact, and hardness of coatings improved with the addition of the SNPs. Nanomechanical properties, such as hardness and elastic modulus, improved when compared to the unmodified coatings. The thermal and abrasion resistances of the coatings improved with the increase in the SNPs content of the coatings. The highest mechanical, thermal, and abrasion properties were obtained for the coatings with 5% SNP content.
| Reference Key |
al-zahrani2020coatingsenhancement
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | Mohammad Asif Alam,Ubair Abdus Samad,Manawwer Alam,Arfat Anis,Saeed M. Al-Zahrani;Mohammad Asif Alam;Ubair Abdus Samad;Manawwer Alam;Arfat Anis;Saeed M. Al-Zahrani; |
| Journal | coatings |
| Year | 2020 |
| DOI |
10.3390/coatings10040310
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.