Effect of Carbon Addition and Mixture Method on the Microstructure and Mechanical Properties of Silicon Carbide
Clicks: 249
ID: 118436
2020
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Emerging Content
30.0
/100
249 views
20 readers
AI Quality Assessment
Not analyzed
Readership in this journal
EmergingRanked #459 of 812 articles by views in Materials (Basel, Switzerland)
Most read
Least read
Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 812 in total.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
High dense (>99% density) SiC ceramics were produced with addition of C and B4C by spark plasma sintering method at 1950 °C under 50 MPa applied pressure for 5 min. To remove the oxygen from the SiC, it was essential to add C. Two different mixture method were used, dry mixing (specktromill) and wet mixing (ball milling). The effect of different levels of carbon additive and mixture method on density, microstructure, elastic modulus, polytype of SiC, Vickers hardness, and fracture toughness were examined. Precisely, 1.5 wt.% C addition was sufficient to remove oxide layer from SiC and improve the properties of dense SiC ceramics. The highest hardness and elastic modulus values were 27.96 and 450 GPa, respectively. Results showed that the 4H polytype caused large elongated grains, while the 6H polytype caused small coaxial grains. It has been observed that it was important to remove oxygen to achieve high density and improve properties of SiC. Other key factor was to include sufficient amount of carbon to remove oxide layer. The results showed that excess carbon prevented to achieve high density with high elastic modulus and hardness.
| Reference Key |
yaşar2020materialseffect
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | Zeynep Aygüzer Yaşar;Richard A. Haber;Yaşar, Zeynep Aygüzer;Haber, Richard A.; |
| Journal | Materials (Basel, Switzerland) |
| Year | 2020 |
| DOI |
10.3390/ma13173768
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.