Nickel-Based Alloy Dry Milling Process Induced Material Softening Effect
Clicks: 86
ID: 116702
2020
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Emerging Content
25.5
/100
86 views
13 readers
AI Quality Assessment
Not analyzed
Readership in this journal
EmergingRanked #739 of 812 articles by views in Materials (Basel, Switzerland)
Most read
Least read
Bar heights use a square-root scale. Only the 120 most-read articles are drawn; the journal has 812 in total.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
Improving the cutting efficiency is the major factor for improving the processing of nickel-based alloys. The novelty of this research is the calibrated SiAlON ceramic tool dry milling nickel-based alloy process. Firstly, the nickel-based alloy dry milling process was analyzed through the finite element method, and the required milling force and temperature were deduced. Then, several dry milling experiments were conducted with the milling temperature, and the milling force was monitored. The change in cutting speeds was from 400 m/min to 700 m/min. Experimental results verified the reduction of the dry milling force hypothesized by the simulation. The experiment also indicated that with a cut depth of 0.3 mm, cut width of 6 mm, and feed per tooth of 0.03 mm/z, when milling speed exceeded 527.52 m/min, the milling force began to decrease, and the milling temperature exceeded the nickel-based alloy softening temperature. This indicated that easy cutting could be realized under high-speed dry milling conditions. The interpolation curve about average temperature and average milling forces showed similarity to the tensile strength reduction with the rise of temperature.
| Reference Key |
zha2020materialsnickel-based
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | Jun Zha;Zelong Yuan;Hangcheng Zhang;Yipeng Li;Yaolong Chen;Zha, Jun;Yuan, Zelong;Zhang, Hangcheng;Li, Yipeng;Chen, Yaolong; |
| Journal | Materials (Basel, Switzerland) |
| Year | 2020 |
| DOI |
10.3390/ma13173758
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.