Comparison of Precipitates and Texture Evolution in Nb-Bearing Grain-Oriented Silicon Steel Produced by Conventional Processing and Novel Twin-Roll Casting
Clicks: 259
ID: 111085
2020
Article Quality & Performance Metrics
Overall Quality
Not rated
Combines reader engagement with the AI quality analysis. This
article has not been analysed, so there is no overall score —
reader engagement is measured and shown alongside.
Reader Engagement
Steady Performance
30.0
/100
259 views
48 readers
AI Quality Assessment
Not analyzed
Readership in this journal
SteadyRanked #37 of 66 articles by views in metals
Most read
Least read
Bar heights use a square-root scale.
Mint this article as an NFT
Not yet mintedCreate a permanent, verifiable on-chain record of this article on the Scimatic Network. The NFT is held in your Journament account, and you can withdraw it to your own wallet at any time.
5
SUSD
one-off · no wallet required
Abstract
The Nb-bearing grain-oriented silicon steel sheets were produced by conventional route and novel twin-roll casting route, respectively. The microstructure, texture and precipitate evolution were comparatively investigated by using electron backscattered diffraction (EBSD) and transmission electron microscope (TEM). The findings revealed that the precipitation behavior and the texture evolution were totally different between the two processing routes. In the conventional route, a great number of nanoscale niobium nitride particles (NbN), which acted as mainly grain growth inhibitors were precipitated during hot rolling, while in the twin-roll casting route, due to the rapid solidification, the precipitation of NbN were suppressed and a new type Nb-bearing precipitate enriched with sulfur element was observed in the as-cast strip. Besides, the primary recrystallized texture of conventional specimens was characterized by strong γ-fiber with a peak at {111} <110>, together with very few Goss components. While in the case of twin-roll casting specimens, the strongest primary recrystallized texture was {111} <112> texture and the area fraction of Goss component was much higher than that of conventional specimens. After final high temperature annealing, complete secondary recrystallization was obtained in twin-roll casting specimens and the magnetic induction of B8 was 0.1 T higher than that of conventional specimens.
| Reference Key |
wang2020metalscomparison
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | Yang Wang;Yuanxiang Zhang;Feng Fang;Xiang Lu;Guo Yuan;Guodong Wang;Wang, Yang;Zhang, Yuanxiang;Fang, Feng;Lu, Xiang;Yuan, Guo;Wang, Guodong; |
| Journal | metals |
| Year | 2020 |
| DOI |
10.3390/met10081085
|
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.