two stage s-n curve in corrosion fatigue of extruded magnesium alloy az31
Clicks: 194
ID: 256502
2009
Article Quality & Performance Metrics
Overall Quality
Improving Quality
0.0
/100
Combines engagement data with AI-assessed academic quality
Reader Engagement
Emerging Content
0.6
/100
2 views
2 readers
Trending
AI Quality Assessment
Not analyzed
Abstract
Tension-compression fatigue tests of extruded AZ31 magnesium alloys were carried out under corrosive environments:(a) high humidity environment (80 %RH) and (b) 5 wt. %NaCl environment. It was found that the reduction rate of fatiguestrength due to corrosive environment was 0.12 under a high humidity and 0.53 under a NaCl environment. It was alsoobserved that under corrosive environments, the S-N curve was not a single curve but a two-stage curve. Above the fatiguelimit under low humidity, the crack nucleation mechanism was due to a localized slip band formation mechanism. Below thefatigue limit under low humidity, the reduction in fatigue strength was attributed to the corrosion pit formation and growth to the critical size for fatigue crack nucleation under the combined effect of cyclic load and the corrosive environment. The critical size was attained when the stress intensity factor range reached the threshold value for crack growth.| Reference Key |
mutoh2009songklanakarintwo
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;Yoshiharu Mutoh;M.S. Shahnewaz Bhuiyan |
| Journal | ferroelectrics |
| Year | 2009 |
| DOI | DOI not found |
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.