Residual stress measurements were conducted by time-of-flight neutron diffraction and Rietveld analysis method in Al2O3/Y-TZP ceramic composites fabricated by different green processing techniques (a novel tape casting and conventional slip casting) and with different Y-TZP content (5 and 40 vol.% Y-TZP). The results show that the residual stresses in Y-TZP particulates are tensile and the ones in Al2O3 matrix are compressive, with almost flat through-thickness residual stress profiles in all bulk samples. As Y-TZP content increased, tension in Y-TZP phase was decreased but compression in Al2O3 matrix was increased (in absolute value). The values of residual stresses for both phases were mainly dependent on the Y-TZP content in the studied Al2O3/Y-TZP composites, irrespective of sample orientation and fabrication processes (a novel tape casting and conventional slip casting).
| Reference Key |
fan2016boletnneutron
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | ;Kunyang Fan;Jesús Ruiz-Hervias;Jonas Gurauskis;Antonio J. Sanchez-Herencia;Carmen Baudín |
| Journal | medicinal chemistry (shariqah (united arab emirates)) |
| Year | 2016 |
| DOI | 10.1016/j.bsecv.2015.10.006 |
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.