synthesis of gelatin-γ-polyglutamic acid-based hydrogel for the in vitro controlled release of epigallocatechin gallate (egcg) from camellia sinensis

Abstract

The antioxidant property and other health benefits of the most abundant catechin, epigallocatechin gallate (EGCG), are limited because of poor stability and permeability across intestine. Protecting the EGCG from the harsh gastrointestinal tract (GIT) environment can help to increase its bioavailability following oral administration. In this study, EGCG was loaded to hydrogel prepared from ionic interaction between an optimized concentration of gelatin and γ-polyglutamic acid (γ-PGA), with ethylcarbodiimide (EDC) as the crosslinker. Physicochemical characterization of hydrogel was done using Fourier transform-infrared spectroscopy (FT-IR), differential scanning calorimetry (DSC) and scanning electron microscopy (SEM). The dependence of the swelling degree (SD) of the hydrogel to the amount of gelatin, γ-PGA, EDC, swelling time and pH was determined. A high SD of the crosslinked hydrogel was noted at pH 4.5, 6.8 and 9.0 compared to pH 7.4, which describes pH-responsiveness. Approximately 67% of the EGCG from the prepared solution was loaded to the hydrogel after 12 h post-loading, in which loading efficiency was related to the amount of EDC. The in vitro release profile of EGCG at pH 1.2, 6.8 and 7.4, simulating GIT conditions, resulted in different sustained release curves. Wherein, the released EGCG was not degraded instantly compared to free-EGCG at controlled temperature of 37 °C at different pH monitored against time. Therefore, this study proves the potential of pH-responsive gelatin-γ-PGA-based hydrogel as a biopolymer vehicle to deliver EGCG.