Comparative Study on Flow-Accelerated Corrosion and Erosion-Corrosion at a 90° Carbon Steel Bend.
Clicks: 181
ID: 105205
2020
Electrochemical measurements and surface analysis are performed to comparatively study flow-accelerated corrosion (FAC) and erosion-corrosion (E-C) behavior at a 90° carbon steel bend. The corrosion rates are higher under FAC conditions than those under E-C conditions. For FAC, the corrosion is more serious at the inside wall. However, corrosion is exacerbated at the outside wall under E-C conditions. No erosion scratches are observed under FAC conditions and at the inside wall under E-C conditions, while remarkable erosion scratches appear at the outside wall under E-C conditions. The dominant hydrodynamics affecting FAC and E-C are remarkably different.
| Reference Key |
zeng2020comparativematerials
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | Zeng, Li;Chen, Geng;Chen, Hanxin; |
| Journal | Materials (Basel, Switzerland) |
| Year | 2020 |
| DOI | E1780 |
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.